ASTM A-333

Normas e condições técnicas para o fornecimento: ASME SA 333 American society of mechanical engineers; ASTM A-333 M American society for Testing and Materials
Aplicação: Especificação padrão de sem costura e com solda para baixas temperaturas.
Composição química (%):

Grade 1 Grade 3 Grade 4 Grade 6 Grade 7 Grade 8 Grade 9 Grade 10 Grade 11
Carbon, max 0.3 0.19 0.12 0.3 0.19 0.13 0.2 0.2 0.1
Manganese 0.40–1.06 0.31–0.64 0.50–1.05 0.29–1.06 0.90 max 0.90 max 0.40–1.06 1.15–1.50 0.60 max
Phosphorus, max 0.025 0.025 0.025 0.025 0.025 0.025 0.025 0.035 0.025
Sulfur, max 0.025 0.025 0.025 0.025 0.025 0.025 0.025 0.015 0.025
Silicon … 0.18–0.37 0.08–0.37 0.10 min 0.13–0.32 0.13–0.32 … 0.10–0.35 0.35 max
Nickel … 3.18–3.82 0.47–0.98 … 2.03–2.57 8.40–9.60 1.60–2.24 0.25 max 35.0–37.0
Chromium … … 0.44–1.01 … … … … 0.15 max 0.50 max
Copper … … 0.40–0.75 … … … … 0.15 max 0.50 max
Aluminum … … 0.04–0.30 … … … … 0.06 max …
Vanadium, max … … … … … … … 0.12 …
Columbium, max … … … … … … … 0.05 …
Molybdenum, max … … … … … … … 0.05 0.50 max
Cobalt … … … … … … … … 0.50 max

Propriedades mecânicas:

Grade 1 Grade 3 Grade 4 Grade 6 Grade 7 Grade 8 Grade 9 Grade 10 Grade 11
psi MPa psi MPa psi MPa psi MPa psi MPa psi MPa psi MPa psi MPa psi MPa
Tensile strength min 55 000 380 65 000 450 60 000 415 60 000 415 65 000 450 100 000 690 63 000 435 80 000 550 65 000 450
Yield strength min 30 000 205 35 000 240 35 000 240 35 000 240 35 000 240 75 000 515 46 000 315 65 000 450 35 000 240

 

Impact Temperature
Grade Minimum Impact Test Temperature
°F °C
1 -50 -45
3 -150 -100
4 -150 -100
6 -50 -45
7 -100 -75
8 -320 -195
9 -100 -75
10 -75 -60